D1717-8942
Brand Feilong
Product origin China
Delivery time 30-45-days
Supply capacity 30000PCS/Month
100% NON-ASBESTOS MATERIAL
PREMIUM QUALITY BRAKE PADS
BEST STOPPING POWER IN A WIDE VARIETY OF ROAD CONDITIONS
The brake pads have good comfort and initial performance.
The coefficient of friction is around 0.45.
The damage to the pair of parts is small, and the pair of brake pads (brake discs) have a long service life and are more than 20% longer than the semi-metal brake pads.
the brake pad manufacturing method includes the following steps:
(1) pulverizing the silicon oxide powder to a fineness of 1200 mesh;
(2) pulverizing silicon nitride to a fineness of 1600 mesh;
(3) The silicon oxide and silicon nitride powder after grinding are uniformly mixed at a mass ratio of 1:0.05 to 0.10, heated to 1200 ° C, and the heated powder is added to a mold of 50 cm × 50 cm × 20 cm and pressurized at 10 MPa, and the pressure is maintained. Until the powder temperature drops to 700 ° C, the product that continues to cool naturally is the inorganic car brake pad raw material;
The D1717 -8942 brake pads are made of internationally advanced ceramic formulas and can meet the needs of the driving environment after hundreds of severe high temperature, noise and wear tests. More than ten years of production experience combined with continuous optimization of production technology, comprehensively solve the problems of ordinary brake pads, ash, non-wear, etc., to provide more excellent braking force, shorter effective braking distance and more for your car. Comfortable driving experience and more advanced security
(4) According to the design of the automobile brake, it is necessary to process the raw materials obtained above into a suitable shape.
The invention has the advantages of simple production process, low production cost and wide promotion; the brake pad is resistant to high temperature and is not easy to soften, and the vehicle can be safely driven.